Honeycomb Ceramic Substrate Used In Vehicle
Honeycomb ceramic substrate is made of cordierite, and is used for car catalytic converter. The cells density can be 100 cpsi, 300 cpsi or 400 cpsi. The shape will be round, oval or racetrack. We can supply both ceramic element coated with noble metals of PT, Pd, Rh and ceramic element without noble metals.
The corundum/mullite and cordierite/mullite complex thermal storage honeycomb ceramic developed by our company has the following notable characters: Perfect high temperature resistance, anticorrosion, perfect thermal shock stability, high mechanical strength, large thermal storage capacity, advantaging heat conduction property, energy conserving result and service life are improved greatly.
Specifications
*Advanced ceramic catalyst substrate manufacturer
*Thin wall thickness, high surface area, good thermal shock
*Strong production capacity, we both produce catalyst and catalyst substrate
*Leading technology level, the most experienced experts and advanced production
*Using advanced scientific formula, offer best products and service to every customer
Honeycomb ceramic substrate is made of cordierite, and is used for car catalytic converter. The cells density can be 100 cpsi, 300 cpsi or 400 cpsi. The shape will be round, oval or racetrack. We can supply both ceramic element coated with noble metals of PT, Pd, Rh and ceramic element without noble metals.
The corundum/mullite and cordierite/mullite complex thermal storage honeycomb ceramic developed by our company has the following notable characters: Perfect high temperature resistance, anticorrosion, perfect thermal shock stability, high mechanical strength, large thermal storage capacity, advantaging heat conduction property, energy conserving result and service life are improved greatly.
Specifications
*Advanced ceramic catalyst substrate manufacturer
*Thin wall thickness, high surface area, good thermal shock
*Strong production capacity, we both produce catalyst and catalyst substrate
*Leading technology level, the most experienced experts and advanced production
*Using advanced scientific formula, offer best products and service to every customer
Index | Metric Unit | Value | British Unit | Value |
Material Density | g/cm3 | 2.3-2.6 | Lb/ft3 | 151 |
Average Linear Expansion (20-800) | 10-6/k-1 | <2.5 | ||
Special Heat Capacity | KJ/Kg | 900-1200 | ||
Heat Conductivity | W/MK | 1.8-3.0 | ||
Maximum Application Temp. | celsius degre | 1350 | 2450 | |
Acid resist strength wt.loss | % | <4 | ||
Water Absorption | % | <5 |
Item | Test result | Test method | |
Cordierite principal crystalline phase (wt %) | ≥90 | X-Ray | |
RT Mpa (Mpa) | A axis | ≥16 | universal materials tester |
B axis | ≥2 | ||
C axis | ≥0.15 | ||
Water absorption(%) | ≥20 | gravimetric hygrometer | |
Softening temperature(celsius degree) | ≥1360 | high-temperature electric resistance furnace | |
Coefficient of thermal expansion (R~800celsius degree) (cm/cm/celsius degree) | ≤1.5×10-6 (550celsius degree) | thermal dilatometer | |
≤1.2×10-6 (800celsius degree) | |||
Maximum service temperature (celsius degree) | 1400 | / | |
Thermal shock resistance (R~850celsius degree) | 30 mins not crack, 5 circles | Air cooling |