CMC Carboxymethyl cellulose sodium
Carboxy Methyl Cellulose(CMC) is synthesized by the alkali-catalyzed reaction of cellulose with chloroacetic acid. The polar (organic acid) carboxyl groups render the cellulose soluble and chemically reactive. The functional properties of Fooding Carboxy Methyl Cellulose(CMC) depend on the degree of substitution of the cellulose structure (i.e., how many of the hydroxyl groups have taken part in the substitution reaction), as well as the chain length of the cellulose backbone structure and the degree of clustering of the carboxymethyl substituents.
Oil Drilling Grade CMC
Physical and Chemical Indexes of Sodium Carboxymethyl Cellulose for Drilling Fluid.(Perform SY5093-92 Standard)
Note:Perform OCMA NO.DFCP-2/NO.DFCP-7 Standard.
Product performance and characteristics:
CMC has a high ability to control water loss. In particular, PAC is a highly effective fluid loss reducer at lower dosages. You can control the loss of water to a higher level. It does not affect other properties of the mud.
The formed mud cake is of good quality, strong and tough.
It has good temperature resistance and excellent salt resistance. Under a certain salt concentration, it still has a good ability to reduce water loss and maintain a certain rheology. Compared to soluble in salt water and soluble in water, the viscosity hardly changes. Particularly suitable for offshore drilling and deep well requirements.
It can well control the rheological properties of the mud. It has good non-Newtonian fluidity.
In addition, KELAIDE® CMC is used as a cementing fluid to prevent fluids from entering pores and fractures. It is used as a fracturing fluid to control fluid loss into the well.
Building grade CMC
Note:we can produce it according to your requirements.
1. "KELAIDE®" CMC is applied to water-based latex paint. It can meet the rheological properties of a certain flow under the action of brush or roller shear force.
2. It can control viscosity and suspension.
3. Generally, CMC accounts for 1-3% in water-based paints and coatings.
Carboxy Methyl Cellulose(CMC) is synthesized by the alkali-catalyzed reaction of cellulose with chloroacetic acid. The polar (organic acid) carboxyl groups render the cellulose soluble and chemically reactive. The functional properties of Fooding Carboxy Methyl Cellulose(CMC) depend on the degree of substitution of the cellulose structure (i.e., how many of the hydroxyl groups have taken part in the substitution reaction), as well as the chain length of the cellulose backbone structure and the degree of clustering of the carboxymethyl substituents.
Oil Drilling Grade CMC
Physical and Chemical Indexes of Sodium Carboxymethyl Cellulose for Drilling Fluid.(Perform SY5093-92 Standard)
LV-CMC | MV-CMC | HV-CMC | |
Appearance | White or light yellow powder, freely flowable | ||
Replace degrees(D. S) | 0.80 min | ||
Purity | 80% min | 85% min | 95% min |
Viscosity 2% (in 2% solution at 25 centigrade) | 200-500 mpa.s | 600-900 mpa.s | 1000-1800 mpa.s |
Size(60 head) | 80% | ||
Moisture (%) | 10% max | ||
PH | 7.0-9.0 | 7.0-9.0 | 6.5-8.0 |
Category | Item | Index | ||
Distilled water | Salt water | Saturated salt water | ||
Oil-based mud | Filtration loss,ml | 60±10 | 90±10 | 100±10 |
Apparent viscosity,mpa.s | ≤6 | ≤6 | ≤10 | |
PH | 8.0±1.0 | 8.0±1.0 | 7.5±1.0 | |
HV-CMC | Pulping rate,m³/t | ≥200 | ≥150 | ≥160 |
LV-CMC | Filtration loss (10ml) | Dosage,g/l | ≤7.0 | ≤10.0 |
Apparent viscosity,mpa.s | ≤4.0 | ≤6.0 | ||
MV-CMC | Dosage,g/l | 6.0 | 14.0 | 3.5 |
Apparent viscosity,mpa.s | ≥15 | ≥15 | ≥15 | |
Filtration loss,ml | ≤9 | ≤9 | ≤8 |
Product performance and characteristics:
CMC has a high ability to control water loss. In particular, PAC is a highly effective fluid loss reducer at lower dosages. You can control the loss of water to a higher level. It does not affect other properties of the mud.
The formed mud cake is of good quality, strong and tough.
It has good temperature resistance and excellent salt resistance. Under a certain salt concentration, it still has a good ability to reduce water loss and maintain a certain rheology. Compared to soluble in salt water and soluble in water, the viscosity hardly changes. Particularly suitable for offshore drilling and deep well requirements.
It can well control the rheological properties of the mud. It has good non-Newtonian fluidity.
In addition, KELAIDE® CMC is used as a cementing fluid to prevent fluids from entering pores and fractures. It is used as a fracturing fluid to control fluid loss into the well.
Building grade CMC
LV-CMC | MV-CMC | HV-CMC | |||
Appearance | White or light yellow powder, freely flowable | ||||
Purity | 75-85% min | 75-90% min | 80-90% min | ||
Viscosity 2% (in 2.5% solution at 30 centigrade) | 300-500 mpa.s | 400-700 mpa.s | 800-1200 mpa.s | ||
Moisture (%) | 7-10% | 6-10% | 7-10% |
Model | 2% viscosity,mpa.s | PH | Loss on drying,% | Purity% |
KLD7 | 600-800 | 7-9 | ≤10 | ≥65 |
KLD8-2 | ≥800 | 7-9 | ≤10 | ≥70 |
KLD8-4 | 800-1200 | 7-9 | ≤10 | ≥80 |
KLDT04 | ≥450 | 8-10 | ≤10 | |
KLDT02 | 250-300 | 8-10 | ≤10 | |
KLD348 | ≥300 | 8-12 | ≤40 | |
KLD248 | 100-200 | 8-12 | ≤40 | |
KLD148 | 40-100 | 8-12 | ≤40 |
1. "KELAIDE®" CMC is applied to water-based latex paint. It can meet the rheological properties of a certain flow under the action of brush or roller shear force.
2. It can control viscosity and suspension.
3. Generally, CMC accounts for 1-3% in water-based paints and coatings.